Platinum Tanking Slurry is a high quality, cementitious compound that is mixed with water to form as smooth paste (tanking slurry).
Platinum Tanking Slurry is applied directly to concrete or masonry structures and penetrates a short distance into capillary cracks, fissures and pores in the surface of the concrete. The presence of water and free lime causes Platinum Tanking Slurry to form insoluble crystals which block the pores and prevent the passage of water effectively making the concrete watertight for the lifetime of the structure.
on orders over £100(ex. VAT, mainland UK only)
Free Help & Advice
Call 01355 222 777Mon.-Fri 8:30am - 4:15pm, or email us
Next Day Delivery
Order Before 2:30pm for Same Day Despatch (terms apply)
A proudly independent family business with 40 years experience
Platinum Tanking Slurry is a high quality, cementitious compound that contains Portland Cement, Graded Quartz Sands, Aggregates and Chemical Additives, supplied as a powder.
Platinum Tanking Slurry is mixed with water to form as smooth paste (slurry). The slurry is applied directly to concrete or masonry structures and penetrates a short distance into capillary cracks, fissures and pores in the surface of the concrete.
The presence of water and free lime causes Platinum Tanking Slurry to form insoluble crystals which block the pores and prevent the passage of water.
This effectively makes the concrete watertight for the lifetime of the structure.
Platinum Tanking Slurry can be applied by brush or spray onto new or old structurally sound surfaces, either to the internal or the external side. It can be applied to both horizontal or vertical surfaces.
Surfaces should be prepared to have a capillary open structure. The waterproofing barrier should run continuously around the whole structure.
Platinum Tanking Slurry is for use where the basement is above the level of the water table.
Platinum Tanking Slurry can be used for the three grades of protection in basements described in BS8102.
Grade 1: For Car Parking.
Grade 2: For Plant Rooms, Workshops and Garages.
Grade 3: For Residential and Commercial Areas.
Platinum Tanking Slurry has passed the tests of WRAS (Water Regulations Advisory Scheme), BS6920 and is approved for drinking water structures such as reservoirs and concrete drinking water tanks.
Platinum Tanking Slurry can also be used in Swimming Pools, Retaining Walls, Tunnels and Lift Shafts.
Surface Preparation is crucial and must be carried out thoroughly. The surface must present an open capillary structure to allow penetration of the crystalline chemicals.
All surfaces should be clean and free of paint systems, oils, loose dust, shutter treatments, curing compounds, surface hardeners and other contaminants. Surface Preparation can be carried out best by high pressure water jetting, grit blasting or mechanical scrabbling.
Large cracks and other defects can be repaired using a 3:1 sand : cement mortar gauged with Platinum SBR. Repaired areas can be coated with Platinum Tanking Slurry after 24 Hours, but large areas of new brickwork, poured concrete or cement renders should be allowed to cure for 3 days before application of Platinum Tanking Slurry.
Timber battens and fixings must be removed before treatment commences. Provision for re-fixing of battens should be made in the wall prior to application of Platinum Tanking Slurry. Drilling for fixtures should NOT be carried out after Platinum Tanking Slurry has been applied as the holes would provide a release for any hydrostatic pressure behind, with resultant of leaking water.
In locations where running water is evident, this would suggest some degree of hydrostatic pressure that must be dispersed to present a satisfactory damp substrate onto which the Platinum Tanking Slurry can be applied.
Platinum Aqua Stop Plugging Compound is mixed 4:1 with water with a gloved hand into a ball and then placed directly onto the leaking substrate. Hold for 30 seconds or until the compound is firm to the touch.
This diagram on Page 2 of the Technical Data Sheet shows the recommended procedure for plugging a water leak.
It is important not to mix more material than can be applied within 30 minutes at 20°C, or less in hot conditions. The recommended mix ratio is approximately 2.5 to 3 parts Platinum Tanking Slurry to 1 part clean water by volume.
Pour the required amount of water into a clean bucket and add the powder slowly, mixing to a smooth lump-free consistency, i.e 25kg of Platinum Tanking Slurry will require 8 Litres of water for mixing.
If the mixed material becomes stiff, do not re-mix with water, but discard and prepare fresh material.
It is critical that all surfaces being treated with Platinum Tanking Slurry are clean and have been properly prepared (see ‘Surface Preparation’ above). Always apply the mix to a pre-dampened surface. Porous substrates require more dampening than dense ones. Normal problems of damp and water ingress can be addressed by applying two coats of Platinum Tanking Slurry over the whole area.
Brush the first coat of mix firmly onto the pre-dampened area, using a Tanking Block Brush. The normal thickness of the first coat should be between 1mm and 1.5mm.
The second coat may be applied as soon as the first coat has become ‘touch-dry’. In warm conditions, spray a fine mist of water over the surface of the first coat. Apply the second coat at right angles to the first to ensure complete coverage. This may be applied by trowel to give a dense smooth finish.
It is recommended that Platinum Fillet Seal is used at internal junctions of floors and walls.
If it is impractical to provide a fillet between floor and wall, then a saw cut should be made in the floor slab as close to the wall as possible and Platinum Tanking Slurry allowed to flow into the saw cut (See diagram on Page 1 on the Technical Data Sheet).
A two-layer application requires about 3kg / m² of powder, but this depends on the roughness of the surface.
Uniform hardening and water tightness can be assured if the product is not allowed to dry out too rapidly, under moist conditions for at least three days. It is recommended that ventilation is provided as a lack of it may cause small condensation beads to form on the surface of the Tanking Slurry. Protect the coating against excessively fast evaporation in hot conditions or drying winds. If these conditions prevail, mist spray the surface regularly.Dehumidifiers should not be used immediately after the application of Platinum Tanking Slurry as this would arrest the curing system.
Remedial Plaster Systems may be used over Platinum Tanking Slurry provided an intermediate bonding compound is employed. Dilute Platinum SBR with an equal volume of water and apply to the cured Tanking Slurry and allow to become tacky, but not dry. Plaster may then be applied as normal.
Where Cement Rendering is required, use an intermediate bonding slurry mixed at 2 parts Sand : 1 Part Cement gauged with a 1:1 SBR : Water mix. Apply the Slurry to the Tanking and apply the first render coat before the slurry dries.
A period of at least 6 month should be allowed before permanent decoration is considered. During this period use only permeable emulsion paints.
Spillages should be cleaned up promptly. Non hardening material may be removed from surfaces or tools with water.
Surface preparation ensures an open capillary structure for proper penetration of crystalline chemicals. It requires a clean surface free of contaminants like paint, oils, and dust.
Large cracks can be repaired with a 3:1 sand:cement mortar gauged with Platinum SBR. After 24 hours, the repaired areas can be coated with Platinum Tanking Slurry, but new brickwork or concrete should cure for 3 days.
The recommended mix ratio is approximately 2.5 to 3 parts Platinum Tanking/Damp Proof Slurry to 1 part clean water by volume. Do not mix more material than can be applied within 30 minutes at 20°C.
Apply the mix to a pre-dampened surface. Brush the first coat firmly using a Tanking Block Brush, with a normal thickness between 1mm and 1.5mm. The second coat can be applied when the first is touch-dry.
Ensure uniform hardening and water tightness by preventing rapid drying. Ventilation is essential, and mist spraying the surface regularly is recommended in hot or windy conditions. Avoid using dehumidifiers immediately after application to allow proper curing.